Abstract

Self-healing, where a modification in some parameter is reversed with time without any external intervention, is one of the particularly interesting properties of halide perovskites. While there are a number of studies showing such self-healing in perovskites, they all are carried out on thin films, where the interface between the perovskite and another phase (including the ambient) is often a dominating and interfering factor in the process. Here, self-healing in perovskite (methylammonium, formamidinium, and cesium lead bromide (MAPbBr₃, FAPbBr₃, and CsPbBr₃)) single crystals is reported, using two-photon microscopy to create damage (photobleaching) ≈110 µm inside the crystals and to monitor the recovery of photoluminescence after the damage. Self-healing occurs in all three perovskites with FAPbBr₃ the fastest (≈1 h) and CsPbBr₃ the slowest (tens of hours) to recover. This behavior, different from surface-dominated stability trends, is typical of the bulk and is strongly dependent on the localization of degradation products not far from the site of the damage. The mechanism of self-healing is discussed with the possible participation of polybromide species. It provides a closed chemical cycle and does not necessarily involve defect or ion migration phenomena that are often proposed to explain reversible phenomena in halide perovskites.

Direct proof of self-healing inside lead bromide perovskite crystals is provided. Two-photon excitation, from high-intensity sub-bandgap (800 nm) pulsed illumination, allows damage to and monitoring deep (>100 μm) inside bromide perovskite single crystals via photoluminescence. Complete or partial recovery of photodamage is observed in minutes to hours. A complete chemical mechanism involving ABr₃ species is proposed to explain the phenomenon.

http://ift.tt/2D4WVdv